Study of the effect of static stresses on the hydrogen content and electrochemical characteristics of steels of different types

When cathodic protection is applied in places where paint films are damaged, an intense release of hydrogen occurs, which is removed both through diffusion and by transition from the adsorbed state on the metal surface to the subsurface layers thus leading to static hydrogen fatigue of steels, i.e., a brittle fracture occurs suddenly under static loading conditions at stress values significantly lower than the strength limit and even below the plasticity limit. We present the results of studying the impact of static tensile stresses on the hydrogen absorption by a metal during its cathodic polarization and the distribution of hydrogen over the cross-section of the metal surface. Three types of metal samples were used: wire samples made of U8A steel, plate samples made of 10KhSND steel, and semicircular samples made of Kh18N9T stainless steel with a stress concentrator. Tests of wire and semi-ring samples were carried out under a constant load and plate samples were tested under constant deformation. Polarization of wire and plate samples was carried out at different current densities for 4 days and semi-ring samples for 1 hour. At the end of polarization, the layer-by-layer distribution of hydrogen absorbed by the metal was determined by the anodic dissolution method. It is shown that with increasing deformation, the hydrogen content of the surface layers of the metal increases. Moreover, application of tensile loads and deformation of the metal by bending contribute to an increase in the amount of absorbed hydrogen and affect hydrogen distribution over the metal cross section. The thickness of the layer containing the maximum amount of hydrogen differs in steels of different compositions and structures. The results obtained can be used to protect structural steels against corrosion in sea water.

1. Rakovskaya E. G., Zanko N. G., Yagunova L. K. Determination of the hydrogen content in the near-surface layers of U8A steel using high-frequency currents / Industr. Lab. Mater. Diagn. 2021. Vol. 87. N 7. P. 44 – 48 [in Russian]. DOI: 10.26896/1028-6861-2021-87-7-44-48

2. Kutepov S. N., Klementev D. S., Kalinin A. A. Influence of microstructural factors on the nature of hydrogen cracking of welded joints of high-strength steels (review) / Izv. TGU. Tekhn. Nauki. 2022. N 8. P. 398 – 411 [in Russian]. DOI: 10.24412/2071-6168-2022-8-398-412

3. Sergeev N. N., Izvolsky V. V., Sergeev A. N. Forecasting the durability of rebar under stress corrosion cracking / Vestn. RGATA im. P. A. Solovyova. 2019. N 2(49). P. 93 – 104 [in Russian].

4. Li X., Ma X., Song X., et al. Review of Hydrogen Embrittlement in Metals: Hydrogen Diffusion, Hydrogen Characterization, Hydrogen Embrittlement Mechanism and Prevention / Acta Metallurgica Sinica (English Letters). 2020. Vol. 33. N 6. P. 759 – 773. DOI: 10.1007/s40195-020-01039-7

5. Rakovskaya E. G., Yagunova L. K. Investigation of the influence of tensile stresses on hydrogen absorption during cathodic protection of steel in sea water / Industr. Lab. Mater. Diagn. 2020. Vol. 86. N 6. P. 24 – 28 [in Russian]. DOI: 10.26896/1028-6861-2020-86-6-24-28

6. Petrov A. I., Razuvaeva M. V. Analysis of the effect of yield strength on stress corrosion cracking of martensitic and ferritic steels in acidic environments / Journal of technical physics. 2022. Vol. 92. N 10. P. 1588 – 1594 [in Russian]. DOI: 10.21883/JTF.2022.10.53251.154-22

7. Golubtsov V. A., Ryabchikov I. V., Mizin V. G. Influence of chemically active elements on hydrogen cracking of steel for pipes / Stal’. 2016. N 3. P. 50 – 53 [in Russian].

8. Sergeev N. N., Sergeev A. N., Kutepov S. N., et al. Analysis of theoretical ideas about the mechanisms of hydrogen cracking of metals and alloys / Izvestiya YuZGU. 2017. N 3(72). P. 6 – 33 [in Russian]. DOI: 10.21869/2223-1560-2017-21-3-6-33

9. Shashkova L. V., Manakov N. A., Kozik E. S., Svidenko E. V. Influence of diffusion-mobile and bound hydrogen on the hydrogen brittleness of steel / Industr. Lab. Mater. Diagn. 2019. Vol. 85. N 8. P. 59 – 66 [in Russian]. DOI: 10.26896/1028-6861-2019-85-8-59-66

10. Averina Yu., Zhukov D., Tsevkova V., et al. Hydrogen embrittlement and peculiar properties of determining the concentration of hydrogen in structural steels / 29th International Conference on Metallurgy and Materials. Conference Proceedings. — Brno, 2020. P. 387 – 392. DOI: 10.37904/metal.2020.3494

11. Semenov Ya. S., Larionov V. P. Identification of the mechanisms of delayed fracture of low-alloy high-strength steels / Industr. Lab. Mater. Diagn. 2001. Vol. 67. N 10. P. 43 – 47 [in Russian].

12. Sergeev N. N., Sergeev A. N., Kutepov S. N., et al. Mechanism of hydrogen cracking of metals and alloys. P. 1 (review) / Materialovedenie. 2018. N 3. P. 27 – 33 [in Russian].

13. Merson E., Krishtal M., Merson D., et al. Effect of strain rate on acoustic emission during hydrogen assisted cracking in high carbon steel / Material Science and Engineering: A. 2012. Vol. 550. P. 408 – 417.

14. Khizhnyakov V. I., Negodin A. V. Corrosion cracking of cathodically protected oil and gas pipelines during long-term operation / Vestn. TGASU. 2017. N 4. P. 264 – 267 [in Russian].

15. Beloglazov S. M. Electrochemical hydrogen and metals. Behavior, fight against embrittlement. — Kaliningrad: KGU, 2004. — 321 p. [in Russian].

16. Fortuna A. S., Astafurova E. G., Astafurov S. V., et al. The influence of electrolytic hydrogenation on the features of the dislocation structure formed in austenitic stainless steel 01Kh17N14M3 under uniaxial tension / Vestn. Tambov. Univ. 2018. P. 555 – 558 [in Russian]. DOI: 10.20310/1810-0198-2018-23-123p-555-558

17. Mushnikova S. Yu., Sagaradze V. V., Fillipov Yu. I., et al. Comparative analysis of stress-corrosion cracking of austenitic steels with different nitrogen contents in chloride and hydrogen-containing environments / Fiz. Met. Metalloved. 2015. Vol. 116. N 6. P. 663 – 672 [in Russian]. DOI: 10.7868/S0015323015060054

18. Michler T., San Marchi C., Naumann J., et al. Hydrogen environment embrittlement of stable austenitic steels / International Journal of Hydrogen Energy. 2012. Vol. 37. P. 16231 – 16246.

19. Astafurova E. G., Maier G. G., Melnikov E. V., et al. Effect of hydrogenation on mechanical properties and tensile fracture mechanism of a high-nitrogen austenitic steel / Journal of Materials Science. 2017. Vol. 52. N 8. P. 4224 – 4233. DOI: 10.1007/s10853-016-0676-z

20. Mushnikova S. Yu., Kostin S. K., Sagaradze V. V., Kataeva N. V. Structure, properties and resistance to corrosion cracking of nitrogen-containing austenitic steel, strengthened by thermomechanical treatment / Fiz. Met. Metalloved. 2017. Vol. 118. N 11. P. 1223 – 1235 [in Russian]. DOI: 10.7868/S0015323017110092