A Sample for Determination of the Characteristics of Static and Cyclic Crack Resistance
Abstract
The advantages of standard limit fracture toughness and crack resistance diagram compared to other standard characteristics of crack resistance under static loading are discussed. We developed a sample similar to the compact reference standard but providing determination (in addition to the limit fracture toughness) the threshold range of the stress intensity factor under cyclic loading. A possibility of using experimental results both for evaluation of the crack resistance of the material and for calculation of the strength of structural elements with cracks is demonstrated. The results of some experiments are presented and discussed.
About the Authors
M. N. GeorgievRussian Federation
E. M. Morozov
НИЯУ МИФИ
Russian Federation
Russian Federation
Yu. N. Simonov
Пермский государственный технический университет
Russian Federation
Russian Federation
References
1. ГОСТ 25.506-85. Методы механических испытаний металлов. Определение характеристик трещиностойкости (вязкости разрушения) при статическом нагружении. - М.: Изд-во стандартов, 1985. - 61 с. МР 1 - 95. Определение характеристик трещиностойкости (вязкости разрушения) при статическом нагружении / Механика катастроф. Определение характеристик трещиностойкости конструкционных материалов. - М.: Изд. МИБ СТС. Ассоциация КОДАС, 1995. С. 7 - 82.
2. МР 9-01. Определение предела трещиностойкости при статическом нагружении / Механика катастроф. Определение характеристик трещиностойкости конструкционных материалов. Т. 2. ФЦНТП «Безопасность». - М.: МИБ СТС. КОДАС, 2001. С. 6 - 47.
3. Васильченко Г. С., Морозов Е. М. Расчет на прочность массивных конструкций, содержащих дефекты / Вестник машиностроения. 1977. № 3. С. 72 - 74.
4. Яблонский И. С. Трещиностойкость листовых материалов при статическом нагружении / Проблемы прочности. 1980. № 5. С. 26 - 29.
5. Баско Е. М. Диаграммы трещиностойкости строительных сталей в связи с размерами трещин и видом нагружения / Заводская лаборатория. 1990. Т. 56. № 12. С. 75 - 79.
6. Анохин А. А., Георгиев М. Н. Трещиностойкость металлов в упругопластической области при статическом нагружении / Проблемы прочности. 1986. № 2. С. 11 - 13.
7. Morozov E. M. Limit analysis for structures with flows / Eng. Fract. Mech. 1974. Vol. 6. N 1. P. 297 - 306.
8. Георгиев М. Н., Морозов Е. М. Предел трещиностойкости и расчет на прочность в пластическом состоянии / Проблемы прочности. 1979. № 7. С. 45 - 48.
9. Morozov E. M. Some problems in experimental fracture mechanics / Eng. Fract. Mech. 1980. Vol. 13. N 3. P. 541 - 561.
10. Морозов Е. М. Концепция предела трещиностойкости / Заводская лаборатория. 1997. Т. 63. № 12. С. 42 - 46.
11. Morozov E. M. An ultimate crack resistance concept / Fatigue and fracture of engineering materials and structures. 1999. N 11. P. 997 - 1002.
12. Георгиев М. Н., Морозов Е. М., Матвиенко Ю. Г. Предел трещиностойкости как характеристика прочности материала и несущей способности металлических конструкций при наличии трещин / J. Tech. Univ. Plovdiv. Tech. Sci. 2001. Vol. 7. P. 9 - 29.
13. ГОСТ 9454-78. Металлы. Метод испытаний на ударный изгиб при пониженных, комнатных и повышенных температурах. - М.: Изд-во стандартов, 1982. С. 12.
14. Гольцев В. Ю., Маркочев В. М., Морозов Е. М. Трещиностойкость стали 08Х18Н10Т после 12 лет эксплуатации трубопровода Ду500 ВВЭР440 / Ядерная физика и инжиниринг. 2013. Т. 4. № 3. С. 1 - 5.
15. SINTAP. Structures Integrity Assessment Procedure for European Industry. Project BE95-1426. Final Procedure, British Steel Report, Rotherham. 1999.
16. R6 Revision 4. Assessment of the Integrity of Structures Containing Defects. British Energy, Generation Report. 2001.
17. Георгиев М., Межова Н. Прикладная механика разрушения. - София: БУЛВЕСТ 2000, 2013. - 560 с.
18. Георгиев М. Н., Симонов Ю. Н. Трещиностойкость железоуглеродистых сплавов. - Пермь: Изд-во ПНИПУ, 2013. - 418 с.
19. Sharples J. K., Watson C. T., Budden P. J. Overview of fracture mechanics research activities in the UK / Strength, Durability and Stability of Materials and Structures. Proc. 4th Int. Conf. 2007. Lithuania. P. 66 - 73.
Review
For citations:
Georgiev M.N., Morozov E.M., Simonov Yu.N. A Sample for Determination of the Characteristics of Static and Cyclic Crack Resistance. Industrial laboratory. Diagnostics of materials. 2015;81(4):40-44. (In Russ.)
Views:
516
Email this article 