Reference Standards of Nickel Superalloys of the System Ni - Al - Co - Mo - Nb - Ta - Cr - W - Re for Spectral Analysis

We developed and certified the reference standards (SS) of nickel superalloys for spectral analysis in accordance with the standards of the Russian Federation [1, 2]. An SS set consists of five types of the samples (5 chemistries compositions - 5 fusions). The SS material is first melted in a vacuum induction furnace VIAM-2002 and then the ingots are remelted in UVNK furnace of directional crystallisation to get the samples homogeneous in chemical composition that are then used in manufacturing the standard cylindrical SS samples: diameter 40 mm, height 35 mm. The validation analysis of SS with determination of the mass fraction of the elements and evaluation of the measurement uncertainty is carried out proceeding from the data base of Federal State Unitary Enterprise «VIAM» and results of inter-laboratory experiment (ILE), obtained in various spectroscopic and chemical procedures at: LTD SPO «TsNIITMash» and GU IMET UrO RAS. The results of studying the chemical composition of SS formed the base for certification of the reference samples of heat-resistant nickel superalloys for spectral analysis of SSE category (standard samples of the enterprise containing instructions for their applications.

стандартные образцы состава, химический состав, технология выплавки материала СО, спектральный и химический анализы сплавов, массовая доля элементов, аттестация, градуировочный график, однородность материала СО, сходимость, воспроизводимость, среднее квадратичное отклонение, standard (reference) samples, chemical composition, technology of melting SS material, spectral and chemical analysis of the alloys, mass fraction of the elements, certification, calibration curve, the homogeneouty of SS material, convergence, reproducibility, standard (middle quadrature) deviation

1. ГОСТ 8.315-1997. Стандартные образцы состава и свойств веществ и материалов. Основные положения. - М.: Изд-во стандартов, 1997. - 33 с.

2. Р 50.2.058-2007 ГСИ. Оценивание неопределенностей аттестованных значений стандартных образцов. - М.: Изд-во стандартов, 2007. - 27 с.

3. ГОСТ 8.532-2002. Стандартные образцы состава веществ и материалов. Межлабораторная метрологическая аттестация. Содержание и порядок выполнения работ. - М.: Изд-во стандартов, 2002. - 9 с.

4. Каблов Е. Н. Стратегические направления развития материалов и технологий их переработки на период до 2030 года / Авиационные материалы и технологии. 2012. № S. С. 7 - 17.

5. Оспенникова О. Г. Стратегия развития жаропрочных сплавов и сталей специального назначения, защитных и теплозащитных покрытий /Авиационные материалы и технологии. 2012. № S. С. 19 - 36.

6. Каблов Е. Н., Петрушин Н. В., Светлов И. Л., Демонис И. М. Литейные жаропрочные никелевые сплавы перспективных ГТД / Технология легких сплавов. 2007. № 2. С. 6 - 16.

7. Каблов Е. Н., Петрушин Н. В., Светлов И. Л., Демонис И. М. Никелевые жаропрочные сплавы нового поколения / Авиационные материалы и технологии. 2012. № S. С. 36 - 52.

8. Petrushin N. V., Svetlov I. L., Samoylov A. I., Morosova G. I. Physicochemical properties and creep strength of a single crystal of nickel-base superalloy containing rhenium and ruthenium / I. Mat. Res. (formerly metallkd.) 2010. Vol. 101. N 5. P. 594 - 600.

9. Kablov E. N., Petrushin N. V., Nazarkin R. M. Designing of intermetallic Ni3Al - based superalloy / In: 9th liege conf. materials for advanced power engineering. 2010. P. 646 - 651.

10. Морозова Г. И., Тимофеева О. Б., Петрушин Н. В. Особенности структуры и фазового состава высокорениевого никелевого жаропрочного сплава / МиТОМ. 2009. № 2(644). С. 10 - 16.

11. Голубовский Е. Р., Светлов И. Л., Петрушин Н. В., Черкасова С. А., Волков М. Е. Малоцикловая усталость монокристаллов жаропрочных никелевых сплавов при повышенных температурах / Деформация и разрушение материалов. 2009. № 8. С. 41 - 48.

12. Svetlov I. L., Petrushin N. V., Shchegolev D. V., Khvatskiy K. K. Anisotropy of mechanical properties of single crystal in fourth generation Ni-based superalloy / In: 9th liege conf. materials for advanced power engineering. 2010. P. 652 - 659.

13. Каблов Е. Н., Бондаренко Ю. А., Ечин А. Б., Сурова В. А. Развитие процесса направленной кристаллизации лопаток ГТД из жаропрочных сплавов с монокристаллической и композиционной структурой / Авиационные материалы и технологии. 2012. № 1. С. 3 - 8.

14. Alekseev A. A., Petrushin N. V., Zaitsev D. V., Treninkov I. A., Filonova E. V. Precipitashion in solid solution and structural transformations in single crystal of high rhenium ruthenium-containing nickel superalloys at high temperature creep / In: 9th liege conf. materials for advanced power engineering. 2010. P. 733 - 740.

15. Петрушин Н. В., Елютин Е. С., Чабина Е. Б., Тимофеева О. Б. О фазовых и структурных превращениях в жаропрочных ренийсодержащих сплавах монокристаллического строения / Литейное производство. 2008. № 7. С. 2 - 6.

16. Протасова Н. А., Светлов И. Л., Бронфин М. Б., Петрушин Н. В. Размерное несоответствие периодов кристаллических решеток γ и γ’-фаз в монокристаллах жаропрочных никелевых сплавов / ФММ. 2008. Т. 106. № 5. С. 512 - 519.

17. Бунтушкин В. П., Базылева О. А., Самойлов А. И., Воронцов М. А. Влияние технологических нагревов на тонкую структуру и свойства сплавов на основе интерметаллида Ni3Al: сб.: Авиационные материалы и технологии. Вып. 1. - М.: ВИАМ, 2008. С. 14 - 16.

18. Каблов Е. Н., Светлов И. Л., Петрушин Н. В. Никелевые жаропрочные сплавы для литья лопаток с направленной и монокристаллической структурой / Материаловедение. 1997. № 4. С. 32 - 39.

19. ОСТ1 90129 - ОСТ1 90433-96. Сплавы никелевые жаропрочные. Методы анализа. - М.: ВИАМ, 1996. - 86 с.

20. Алексеев Р. И., Коровин Ю. И. и др. Руководство по вычислению и обработке результатов количественного анализа. - М.: Атомиздат. 1972. - 165 с.

21. Канаев Н. А., Трофимов Н. В. Атомно-абсорбционный и пламенно-фотометрический анализы сплавов. - М.: Металлургия. 1983. - 258 с.

22. Пчелкин А. И., Харламов И. П., Гусинский М. Н., Шипова Е. В. Метод электроискровой подготовки металлических образцов для атомно-абсорбционного анализа / Журнал аналитической химии. 1987. Т. 32. № 12. С. 2138 - 2140.

23. Томсон М., Уолш Д. Н. Руководство по спектрометрическому анализу с индуктивно-связанной плазмой / Пер. с англ. - М.: Недра. 1988. С. 17 - 38.

24. МИ 2589-2000. Общие методические рекомендации по применению положений ГОСТ 8.315 при разработке и применении стандартных образцов. - Екатеринбург: УНИИМ, 2000. - 15 с.

25. ОСТ1 90128-96. Сплавы никелевые жаропрочные. Общие требования к методам анализа. - М.: ВИАМ, 1996. - 4 с.

26. СТП 1-595-21-352-2001 (ВИАМ). Стандарт предприятия. Разработка стандартных образцов состава сплавов для спектральных методов анализа. - М.: ВИАМ, 2001. - 8 с.

27. ОСТ1 90126-85. Сплавы жаропрочные литейные вакуумной выплавки. - М.: ВИАМ, 1985. - 12 с.

28. ГОСТ 8.531-2002. Стандартные образцы монолитных и дисперсных материалов. Способы оценивания однородности. - М.: Изд-во стандартов, 2002. - 11 с.

29. ГОСТ 6689.1 - ГОСТ 6689.24-92. Никель, сплавы никелевые и медно-никелевые. Методы анализа. - М.: Изд-во стандартов, 1992. - 192 с.

30. Сухенко К. А. Спектральный анализ сталей и сплавов. - М.: Госиздательство «Оборонпром», 1954. - 260 с.