Correlation of the Strain Values and Strengthening Parameters in Tension and Indentation Tests in a Plastic Region
Abstract
Analytical dependences of the ultimate uniform strain and yield stress to ultimate stress ratio on the Meyer’s coefficient n are obtained and exemplified in the study of carbon and low-alloyed perlitic steels using sloping light for measuring the indent diameter upon n determination. Meyer’s law appeared to be incorrect and invalid for austenitic steels due to structure-phase transformations in the strained metal under the indent.
About the Authors
V. M. Matyunin
Национальный исследовательский университет «Московский Энергетический Институт»
Russian Federation
Russian Federation
A. Yu. Marchenkov
Национальный исследовательский университет «Московский Энергетический Институт»
Russian Federation
Russian Federation
References
1. Марковец М. П. Определение механических свойств металлов по твердости. - М.: Машиностроение, 1971. - 171 с.
2. Tabor D. The hardness of metals. - Great Britain: Oxford University press, 1951.
3. Матюнин В. М. Оперативная диагностика механических свойств конструкционных материалов. - М.: Издательский дом МЭИ, 2006.-216 с.
4. Зайцев Г. П. Твердость по Бринеллю как функция параметров пластичности материалов / Заводская лаборатория. 1949. Т. 15. №6. С. 704 - 717.
5. O’Neill H. The hardness of metals and its measurement. - London: Chapman and Hall Ltd., 1934.
6. Матюнин В. М., Дубов А. А., Марченков А. Ю. Общие закономерности проявления масштабного фактора при определении прочности и твердости металла / Заводская лаборатория. Диагностика материалов. 2010. Т. 76. № 8. С. 43 - 47.
Review
For citations:
Matyunin V.M., Marchenkov A.Yu. Correlation of the Strain Values and Strengthening Parameters in Tension and Indentation Tests in a Plastic Region. Industrial laboratory. Diagnostics of materials. 2016;82(9):51-57. (In Russ.)
Views:
277
Email this article 